Chemically Cross-Linked Polyethylene Foam is a polyethylene foam material that is expanded in heat oven after extruded with the help of chemical inflators and cross linking agents that are put inside. It has advanced chemical and mechanical features thanks to its cross-linked structure Compared to DurProx (Compared to DurProx (physically Cross-Linked Polyethylene Foam)the cell structure is larger and the surface is not as smooth. It can be used in many areas that sound, heat, humidity insulation and shock protection is intended. It can be produced for different sectors as cut plate, roll, tube, extra-laminated or non-laminated.
| Production Standard |
|---|
| Thickness Single fold: | 3-20 mm (5 mm for 100 kg/m3 and above)
(2.5mm 90kg/m3 and 115kg/m3 production can be made) |
| Thickness Multi-Fold: | 21-150 mm
(Lamination cannot be made for materials which have higher density than 145 kg/m3) |
| Density: | 3 mm 30-200 kg/m3
5mm and above 25-200 kg/m3 |
| Roll Width: | 800-2200 mm |
| Roll Length: | 25/75/50/100/150/200 m |
| Plate Width: | 400-1800 mm |
| Plate Length: | 200-3000 mm |
| Color: | Can be produced upon request |
| Fire Resistance: | FMVSS 302/ ISO 11925-2 |
| Anti-static: | Can be produced upon request |
| Composite: | Nylon film/Metalized film/fabric/NPE Foam Lamination/ double-sided tape lamination |
| Waiting Periodi: | There is no waiting period |
| Packaging: | *Standard
*Stretch Film wrapped
*Nylon Pouch |
| Label: | *Standard label
*Customer private label |